Resistencia a la torsión de los instrumentos endodónticos PathFile sometidos a fatiga cíclica

Torsional strength of PathFile endodontic instruments undergoing cyclic fatigue

ENDODONCIA  |  INVESTIGACIÓN CIENTÍFICA  |    OPEN ACCESS  |    PEER-REVIEWED

Resistencia a la torsión de los instrumentos endodónticos PathFile sometidos a fatiga cíclica

Torsional strength of PathFile endodontic instruments undergoing cyclic fatigue

Autor/es: Gustavo Lopreite, Jorge Basilaki, Pedro Hecht

Vol: 102  |  Nº 1  |  Mar 2014  |  Páginas: 21-27

Presentado: 28/11/2012  |  Aceptado: 23/04/2013  |  Publicado: 20/03/2014

Stable URL: https://raoa.aoa.org.ar/revistas?roi=1021000201   copiar


Texto completo    |    PDF    |    Citar este artículo


  Twitter  |  Whatsapp  |  Facebook  |  E-mail


Resumen

La fatiga cíclica y la torsión son los dos factores más importantes a los que se ve sometido un instrumento rotatorio endodóntico durante su empleo.

Objetivo: Evaluar la influencia de la fatiga cíclica en la resistencia a la fractura por torsión en instrumentos rotatorios de níquel-titanio utilizados en endodoncia para la preparación quirúrgica.

Materiales y métodos: Se conformó una muestra de 30 instrumentos PathFile (Dentsply-Maillefer, Ballaigues, Suiza) nuevos, calibre .16 con 2% de conicidad, divididos aleatoriamente en cinco grupos (n=6). Un total de 24 instrumentos fueron sometidos a fatiga cíclica por rotación continua en un conducto simulado por un tubo cilíndrico de acero inoxidable, con un calibre interno de 0,5 mm y 25 mm de longitud, una curvatura de 45° y 8 mm de radio a 5 mm de su extremo apical, a 300 rpm y 1 Ncm de torque, en diferentes tiempos: los del Grupo A (GA), 15 s; los del Grupo B (GB), 75 s; los del Grupo C (GC), 150 s; y los del Grupo D (GD), 300 s. El Grupo N (GN) se conservó como control absoluto sin uso. Luego, los instrumentos de todos los grupos fueron montados en un dispositivo diseñado para producir la rotación a 2 rpm y 1 Ncm de torque; los 3 mm apicales de sus puntas fueron fijados en un bloque de resina hasta producir la fractura por torsión. Se registraron los tiempos de fractura correspondientes a cada instrumento, que fueron traducidos a grados de rotación de acuerdo con la velocidad empleada en la prueba, y se volcaron los datos en tablas para su análisis.

Resultados: Los resultados fueron evaluados estadísticamente por medio del análisis de varianza de una vía, seguido de la prueba de Tukey de comparaciones múltiples, y se encontraron diferencias significativas (P<0,001) entre los grupos. La comparación de los grados hasta la fractura registró cuatro diferencias significativas: entre los grupos GN y GC; GN y GD; GA y GD; y GB y GD. Ninguna otra comparación resultó significativa.

Conclusión: Al aumentar la fatiga cíclica a la que es sometido el instrumento PathFile de níquel-titanio rotatorio, disminuye el número de grados de giro necesario para su fractura por torsión.

Palabras clave: Níquel-titanio, fatiga cíclica, torsión.

 



Abstract

The cyclic fatigue and torsion are the two most important factors to which rotary endodontic instruments are subjected during clinical use.

Aim: To evaluate the influence of the cyclic fatigue fracture resistance in torsion rotary nickel titanium instrument used for surgical preparation in endodontics.

Materials and methods: A sample of 30 new instruments, PathFile (Dentsply-Maillefer, Ballaigues, Switzerland) .16 and 02 gauge taper, was randomly divided into five groups (n=6). A total of 24 instruments were subjected to cyclic fatigue by continuous rotation in a simulated canal by a cylindrical tube of stainless steel of 0.5 mm and internal bore of 25 mm length with a 45 degree bend radius 8 mm and 5 mm from its apical ends. And they were made rotate at 300 rpm and 1 Ncm of torque at different times with 15 sec (GA), 75 sec (GB), 150 sec (GC) and 300 sec (GD), and a fifth group was used as absolute control without use (GN). Then the instruments in all groups were mounted in a device designed to cause rotation of 2 rpm and 1 Ncm of torque; beingfixed at 3 mm from its end in a block of resin to produce a fracture by torsion. The time was recorded for each instrument fracture, which was translated into degrees of rotation according to the speed used in the test and overturned tables.

Results: The values were statistically analyzed by ANOVA one way followed by Tukey test for multiple comparisons. Significant differences between groups (P<0.001). The comparison between degrees until fracture records four significant differences between the groups GN/GC, GN/GD, GA/GD and GB/GD. No other comparison was significant.

Conclusion: Increased cyclic fatigue to which the instrument is subjected decreases the time required for fracture by torsion.

Key words: Nickel-titanium, cyclic fatigue, torsion.


Nickel-titanium   cyclic fatigue   torsion  

Citar este artículo:

Lopreite G, Basilaki J, Hecht P. Resistencia a la torsión de los instrumentos endodónticos PathFile sometidos a fatiga cíclica. Rev Asoc Odontol Argent. 2014 Mar 20;102(1):21-27. Disponible en: https://raoa.aoa.org.ar/revistas?roi=1021000201
 Copiar Cita


Texto completo    |    PDF   |    Subir


  Twitter  |  Whatsapp  |  Facebook  |  E-mail


Licencia Creative Commons

Las obras publicadas en este sitio están bajo una Licencia Creative Commons Atribución-NoComercial 2.5 Argentina.

Revista indexada en:

ebscohost Revista de la Asociación Odontológica Argentina    lilacs Revista de la Asociación Odontológica Argentina  latindex Revista de la Asociación Odontológica Argentina
Directory of Open Access Journals Revista de la Asociación Odontológica Argentinagoogle scholar Revista de la Asociación Odontológica Argentinanucleo básico Revista de la Asociación Odontológica Argentina
Dialnet Revista de la Asociación Odontológica ArgentinaMalena Revista de la Asociación Odontológica Argentina   ROAD Revista de la Asociación Odontológica Argentina

Open Access RAOA  Creative Commons RAOA

Crossref

Los artículos científicos de RAOA se identifican con DOI (Digital Object Identifier) Crossref.



artículos leído en línea RAOA

Descargas / lecturas online: 882

artículos leído en línea RAOA

Accesos RAOA Id: 58

Nickel-titanium cyclic fatigue torsion

Auspiciantes del Website:

anuncio 3 Revista de la Asociación Odontológica Argentina
anuncio 3 Revista de la Asociación Odontológica Argentina
anuncio 3 Revista de la Asociación Odontológica Argentina


Google académico RAOA  Schema Org RAOA

Internet Archive RAOA  Dublin Core RAOA



Revista de la Asociación Odontológica Argentina

La Revista de la Asociación Odontológica Argentina, RAOA, es la principal vía de expresión de la producción científica argentina en odontología y un vínculo de unión y medio de información para los colegas e instituciones del país y del exterior. 
Versión electrónica ISSN: 2683-7226. 
Versión electrónica DNDA: 45846766.
Título abreviado: Rev Asoc Odontol Argent